Introduction of Helmet Shell Material

2015-11-19 11:20:40

 

Polycarbonate often contracts to PC, a kind of strong thermoplastic resin, is often produced by bisphenol A and phosgene. Now it has 

developed a non phosgene production method, and has been in at the beginning of the sixties of the 20th century to realize 

industrialization. In the late 1990s realize large scale industrialized product. Now it is the second largest production of engineering plastics after polyamide. Its name comes from its 

internal CO3 group density: 1.20-1.22 g/cm^3. Linear expansion ratio: 3.8×10 cm/cm°CHeat distortion temperature: -45°C to 135°C.

 

Polycarbonate colorless transparent, heat resistance, impact resistance, flame retardant BI grade, in the ordinary use of temperature 

have good mechanical properties. Isotropic to PMMA compared, polycarbonate good impact resistance, high refractive index, good 

processing performance, need not additive with UL94-V-0 grade flame retardant performance. However, PMMA is relatively low and can be produced by bulk polymerization of the device, 

PC can be injection molding, extrusion, molding, blow molding, hot forming, printing, bonding, coating and machining, the most 

important processing method is injection molding. It must be pre drying before molding, moisture content should be less than 0.02%.

 

M-1 double polycarbonate, the structure is more safe.